以下为句子列表：
英文: Abstract: The mixed salts of diethanolamine and sodium of lauramidoethylene sulfosuccinate is prepared to modify the products with the mixture of the diethanolamine and hydrogen sulfite of sodium as sulphonating agent.The transparency problem of the produ
中文: 文摘:采用亚硫酸氢钠与二乙醇胺的混合物作磺化剂，对琥珀酸月桂酰胺基乙酯磺酸钠进行改性，制得了钠与二乙醇胺的混合盐，改善了产品的透明度.性能分析表明：改性前后其主要表面物理性能基本相当，且改性后该产品具有较强的抗盐能力，适用于含盐量较高的制品.
更详细...
英文: The technologies for producing iminodiacetic acid, e. g. chloroacetic acid-glycine method, chloroacetic acid ammoniation, ammonium triacetate, direct synthesis based on hydrocyanic acid, diethanolamine dehydrogenation and ethanolamine methods are introduc
中文: 摘要综述了亚氨基二乙酸的生产方法，包括氯乙酸甘氨酸法、氨代氯乙酸法、氮川三乙酸法、氢氰酸直接合成法、二乙醇胺脱氢法和单乙醇胺法。
更详细...
英文: Using diethanolamine as aminating agent and glacial acetic acid as neutralizing agent,aminated epoxy acrylic cationic resin was prepared.The effect of technology of aminated epoxy acrylic resin on properties of eletrodeposition was studied by conductivity
中文: 以二乙醇胺为胺化剂、冰醋酸为中和剂,合成了胺化环氧丙烯酸阳离子树脂.采用电泳仪和电导率仪,研究了胺化环氧丙烯酸树脂合成工艺对阴极电泳涂料电沉积性的影响.结果表明,随着胺化温度的增加,电泳液电导率先下降后上升.将冰醋酸加入树脂中中和,后用水稀释,比树脂在醋酸稀溶液中中和,电沉积性能更好.电沉积速率随着中和温度的上升而增加,电沉积膜致密性相应增加.中和度(DN)愈高,电泳液电导率愈大,粒径越小,而涂膜外观在中和度为80％时达到最佳.
更详细...
英文: The amidate condition was that nonyl phenol polyethyleneoxide monoether:diethanolamine was .0:. ,reaction temperature was 0～0℃,reaction time was ～h.
中文: 酰胺化条件为:琥珀酸壬基酚聚氧乙烯醚单酯∶二乙醇胺(摩尔比)为∶. ,反应温度为0~0℃,反应时间为~h。
更详细...
英文: The amidate conditions were that citric acid polyethyleneoxide monoether:diethanolamine was .0∶.(mole ratio),reaction temperature was 0～0℃,reaction time was ～h.
中文: 酰胺化条件为柠檬酸壬基酚聚氧乙烯醚单酯∶二乙醇胺(摩尔比)为∶.,反应温度为 0~0℃,反应时间为 ~h。
更详细...
|