以下为句子列表：
英文: Abstract: The property of silk fabric grafted (Cross-Linked) with hydroxypropyl methacrylate and protein at different rate of weigh gain,by measuring strength and elongation at break,dyeability,elastic,moisturecontent,whiteness,permeability of gas,IR and
中文: 文摘:通过对织物的拉伸特性、吸湿性、弹性、染色性、白度、透气性、红外和X射线衍射的研究，探讨了在不同增重率条件下甲基丙烯酸羟丙酯在丝蛋白存在下与真丝绸接枝交联后的结构及其特性的影响。
更详细...
英文: Results show that self-crosslinkable latex at room temperature with high elasticity can be prepared when amount of butyl acrylate is 60%, and amount of methyl methacrylate is 40%, and mass ratio of nonionic emulsifier to anionic emulsifer is 3:1, and amou
中文: 研究结果表明：当丙烯酸丁酯的质量为60%，甲基丙烯酸甲酯的质量为40%，非离子乳化剂和阴离子乳化剂的质量配比为3:1，引发剂的质量为0.6%，自交联单体的质量为2%，保护胶体的质量为0.4%时，可以制备出高弹性自交联乳液。
更详细...
英文: The results showed that the grafted silk fabrics had better water-and oil-repellencies than the non-grafted ones, among which the silk fabrics grafted with hexafluorobutyl methacrylate obtained good water-repellency only, and those grafted with dodecfluor
中文: 结果显示接枝后丝织物的拒水拒油性能均优于未接枝的丝织物；其中经甲基丙烯酸六氟丁酯接枝改性的丝织物仅能获得较佳的拒水效果，而经甲基丙烯酸十二氟庚酯接枝改性的丝织物拒水拒油效果均较好。
更详细...
英文: Glycidyl methacrylate (GMA) derivatized dextran (GMA-Dex) was synthesized by coupling GMA to dextran in the presence of -(N,N-dimethylamino) pyridine using DMSO as an aprotic solvent.
中文: 使用过硫酸铵和N，N，N'，N'-四甲基乙二胺作为氧化还原引发剂引发GMA-Dex与NIPA聚合，合成出了质量比r(r=GMA-Dex/(GMA-Dex+NIPA))分别为0.、0.、0.、0.和0.8的新型共聚水凝胶(P(NIPA-co-GMA-Dex))。
更详细...
英文: N,N′ m phenylene bismaleimide and trimethylol propane trimethacrylate 0.8～.0;
中文: N，N′－间亚苯基双马来酰亚胺和三（甲基丙烯酸三羟甲基）丙酯0．8～．0。
更详细...
|