英文: Abstract: The contrast experimental trials of three refining processes are car ried out for ladle bottom bubbling with nitrogen,nitrogen-argon or argon .The results show that the nitrogen content in steel has an important influence on the stretchability o
中文: 文摘:进行了钢包底吹氮、底吹氮-氩和底吹氩三种精炼工艺对比试验，结果显示，钢中对钢丝拉拔性能影响显著。
更详细...
英文: Aided by impact experiment and fracture analysis, it finds that the impact power of the steels decreases significantly as the nitrogen content increases from 81×10^(-6) to 98×10^(-6), and the drop is the greatest at -40~-60℃.
中文: 通过冲击试验性能数据和断口形貌分析发现，当试验钢含氮量从81×10^(-6)增加到98×10^(-6)时，试验钢的冲击功大幅度地下降，在-40~-60℃区间上冲击功下降幅度最大。
更详细...
英文: Chlorophyll content had no significant relation with the net assimilation rate, but was related to the nitrogen content and the specific leaf weight.
中文: 叶绿素含量与净同化速率间没有显著关系，但与含氮量和比叶重有关。
更详细...
英文: Drenches the oil the top digit incompletely fermented beans 80℃ water temperature direct impact type to change the low position trawl door fixed compression immersion to drench the oil, the amino acid condition nitrogen content will be raised ～ times.
中文: 将高位酱坯80℃水温直冲式淋油改为低位网板固定加压浸泡淋油,氨基酸态氮含量提高～倍。
更详细...
英文: Methods Gelatin, collagen and RGD peptide Arginine Glycine Aspartic acid were physically adsorbed on PS surfaces, XPS was employed to investigate the variation of nitrogen content on the modified surfaces to validate the existence of proteins.
中文: 方法采用物理包被法依靠疏水作用在PS表面架构明胶、胶原和RGD(精氨酸-甘氨酸-天冬氨酸)多肽的生物活性层。 通过光电子能谱(XPS)分析修饰表面的元素含量变化,N元素含量显著提高,说明蛋白分子在表面存在。
更详细...
|